Home / Products / Polyols & MDI(Isocyanate)
  • Polyester Polyols

Polyester Polyols

PPGs for car seats and interior molding

Trademark

Hydroxyl value

mgKOH/g

Acid value

mgKOH/g

Water content

%

pH

Unsaturated value

mol/kg

Viscosity

mPa·s/25℃

K+

mg/kg

Colourity

APHA

Application

Feature


HPOP40

20-23

-

≤0.05

6-9

-

≤8000

-

-

Mixed with high activity polyether together. Used in producing high resilience, cold cured foam for cushions of automobiles, motorcycles, bicycles and steeling wheels. It can increase the bearing capacity of foam products.

High-activity polymer polyol with solid content 40% can be used to produce high resilience slabstock foam, with a better supporting performance. It can be also used to produce molded foam, which has a higher activity, shorter stripping time, better opening effect. It can be used for interior materials. Comparing with POP36/28 and POP93/28, HPOP40 has a better hardening effect and opening effect for foams.


EP-3033

31.5-34.5

≤0.1

≤0.1

5-7

-

-

≤10

≤100

Mixed with polymer polyol grafted polyether together. Used in producing high resilience, cold cured foam for cushions of automobiles, motorcycles, bicycles and steering wheels.

With a functionality of 4, molecular weight of 7000, and low ordor, this high-activity polyether polyols can be used to produce high resilience slabstock foam, effectively enhancing the resilience of foams. It can be also used to produce molded foam, which has a higher activity, shorter stripping time. Comparing with EP-330NY, this product can sustain or even increase the hardness, when increasing the resilience.

This product has a higher functionality and may worsen the hole style of foam in a full MDI or M/T system. Therefore, the user is required to adjust formula according to his own formula system. Because of its higher functionality, there may result in gel formation in the synthesis of polyurethane prepolymer. So it should not used in CASE series.

EP-330N(G)

32.5-35.5

≤0.05

≤0.05

5-7

≤0.07

800-1000

≤3

≤50

High activity polyether . Mixed with polymer polyol grafted polyether together. Used in producing high resilience, cold cured foam for cushions of automobiles, motorcycles, bicycles and steering wheels.

 

With a functionality  of 3, molecular weight of 5000, and low ordor, this kind of high-activity polyether polyol can be used to produce high resilience slabstock foam, effectively enhancing the resilience of foams. It can be also used to produce molded foam, which has a higher activity, shorter stripping time. It is particularly suitable for the preparation of a variety of automobile interior materials.


EP-330N(Y)

32.5-35.5

≤0.08

≤0.05

5-7

≤0.07

800-1000

≤3

≤50

Comparing with EP-330N(G), this product can minimize the odor.


EP-3600

26.5-29.5

≤0.06

≤0.05

5-7

≤0.08

1000-1600

≤5

≤50

Mixed with polymer polyol grafted polyether together. Used in producing high resilience, cold cured foam for cushions of automobiles, motorcycles, bicycles and steering wheels. It can also be used to produce automobile sealant.

With a functionality of 3 and molecular weight of 6000, this high-activity polyether polyol can be used to produce high resilience slabstock foam, effectively enhancing the resilience of foams. It can be also used to produce molded foam, which has a higher activity, shorter stripping time. Comparing with EP-330NY, EP-3600 can be used to prepare more resilient foam with less hardness. This product can also be used for CASE series, which can effectively improve its tensile strength and resilience.


EP-551C

54.5-57.5

≤0.05

≤0.05

5-7

≤0.05

400-600

≤3

≤50

Mixed with polymer polyol. Used in producing high resilience, thermal-molded foam for cushions of automobiles, motorcycles, bicycles and steering wheels.

With a functionality of 3 and molecular weight of 3000, this high-activity polyether polyol can be used to produce thermal-molded foams, which has a higher activity, shorter stripping time. Its activity is higher than DEP-5631D, but lower than EP-330NY.


EP-553

54.5-57.5

 

≤0.05

≤0.05

5-7

≤0.05

400-600

≤3

≤50

Mixed with polymer polyol. Used in producing high resilience, thermal-molded foam for cushions of automobiles, motorcycles, bicycles and steeling wheels.

With a functionality of 3 and molecular weight of 3000, this high-activity polyether polyol can be used to produce thermal-molded foams, which has a higher activity, shorter stripping time. Its activity is higher than DEP-5631D, but lower than EP-551C.

 


 

PPGs for blend polyol used in high-speed  rail

Trademark

Hydroxyl value

mgKOH/g

Acid value

mgKOH/g

Water content

%

pH

Unsaturated value

mol/kg

Viscosity

mPa·s/25℃

K+

mg/kg

Colourity

APHA

Application

Feature

HPOP40

20-23

-

≤0.05

6-9

-

≤8000

-

-

This is a high-activity and high solid content polymer polyols, which can be used to prepare damping materials for high-speed rail.

High-activity polymer polyol with solid content 40% can be used to produce high resilience slabstock foam and polyurethane microporous materials, with a better supporting performance. It can be also used to produce molded foam, which has a higher activity, shorter stripping time, better opening effect.

EP-330N(G)

32.5-35.5

≤0.05

≤0.05

5-7

≤0.07

800-1000

≤3

≤50

This is a high-activity and high molecular weight polyols, which can be used to prepare water-proof and damping materials for high-speed rail.

With a functionality of 3, molecular weight of 5000, and low ordor, this kind of high-activity polyether polyol can be used to produce high resilience slabstock foam, effectively enhancing the resilience of foams. It can be also used to produce molded foam, which has a higher activity, shorter stripping time.

 

PPGs for waterproof  materials

Trademark

Hydroxyl value

mgKOH/g

Acid value

mgKOH/g

Water content

%

pH

Unsaturated value

mol/kg

Viscosity

mPa·s/25℃

K+

mg/kg

Colourity

APHA

Application


DL-400

270-290

≤0.05

≤0.05

5-7

-

60-80

≤5

≤50

This is a low unsaturated polypropylene oxide ether diol, with a molecular weight of 400-8000.  As the basis component for the soft segment structure of polyurethane, it can be used for a variety of polyurethane  waterproof products.


DL-1000D

109-115

≤0.05

≤0.02

5-8

-

120-180

-

-

DL-2000D

54.5-57.5

≤0.05

≤0.02

5-8

≤0.01

270-370

-

-

DL-2500D

43-47

≤0.05

≤0.02

5-8

≤0.01

-

-

-

DL-3000D

36-39

≤0.05

≤0.02

5-8

≤0.01

500-600

-

-

DL-4000D

26.5-29.5

≤0.05

≤0.02

5-8

≤0.01

800-1000

-

-

EDL-8000

12.5-15.5

≤0.08

≤0.05

5-8

-

≤5000

-

-

MN-3050DF

54.5-57.5

≤0.05

≤0.05

5-7

≤0.01

400-700

-

-

This is a low unsaturated polypropylene oxide ether triol, with a molecular weight of 3000. It can be used for a variety of  waterproof polyurethane products, effectively improving the tensile strength of the polyurethane products.

 


MN-430

360-420

≤0.10

≤0.10

5-7

-

400-700

≤20

-

When used in waterproof polyurethane products, it can increase the product’s hardness.

MN-500

330-350

≤0.08

≤0.05

5-7

-

-

≤5

≤50

MN-700

225-255

≤0.05

≤0.10

5-7

-

200-400

≤5

≤50

MN-1000

163-173

≤0.05

≤0.10

5-7

-

-

≤5

≤50

NRC-2000

54.5-57.5

≤0.05

≤0.05

5-7

-

-

≤10

≤100

With a functionality of 2 and molecular weight of 2000, this high ethylene oxide content polyether polyol can be used to synthesize water-swellable polyurethane for waterproof plugging materials.

NRC-3000

54.5-57.5

≤0.05

≤0.05

5-7

-

-

≤10

≤100

With a functionality of 3 and molecular weight of 3000, this high ethylene oxide content polyether polyols can be used to synthesize water-swellable polyurethane for waterproof plugging materials.

 

PPGs for  pavement materials

Trademark

Hydroxyl value

mgKOH/g

Acid value

mgKOH/g

Water content

%

pH

Unsaturated value

mol/kg

Viscosity

mPa·s/25℃

K+

mg/kg

Colourity

APHA

Application

Feature

DL-400

270-290

≤0.05

≤0.05

5-7

-

60-80

≤5

≤50

This is a diol polyether with a molecular weight of 400. It can be used for a variety of pavement polyurethane products with a higher toughness.

DL series products are mainly used for CASE series products, with a molecular weight range from 700 to 12000. For application, as the molecular weight of the polyol increases, the elongation at break gradually increases while the tensile strength and hardness decreases. Customers may choose polyether polyols of different molecular weight according to their final product’s request. They can also arrange MN-3050DF, EP-330NG or EP-3600 in groups to increase the product’s tensile strength.

 

DL-1000D

109-115

≤0.05

≤0.02

5-8

-

120-180

-

-

This is a low unsaturated polypropylene oxide ether diol, with a molecular weight of 1000-8000.  As the basis component for the soft segment structure of polyurethane, it can be used for a variety of polyurethane pavement products.

 

DL-2000D

54.5-57.5

≤0.05

≤0.02

5-8

≤0.01

270-370

-

-

DL-2500D

43-47

≤0.05

≤0.02

5-8

≤0.01

-

-

-

DL-3000D

36-39

≤0.05

≤0.02

5-8

≤0.01

500-600

-

-

DL-4000D

26.5-29.5

≤0.05

≤0.02

5-8

≤0.01

800-1000

-

-

EDL-8000

12.5-15.5

≤0.08

≤0.05

5-8

-

≤5000

-

-

MN-3050DF

54.5-57.5

≤0.05

≤0.05

5-7

≤0.01

400-700

 

-

-

This is a low unsaturated polypropylene oxide ether triol, with a molecular weight of 3000. It can be used for a variety of  pavement polyurethane products, effectively improving the tensile strength of the polyurethane products.

It can not be used to prepare flexible polyurethane foam, as it may cause sponge heartburn.

EP-3600

26.5-29.5

≤0.06

≤0.05

5-7

≤0.08

1000-1600

≤5

≤50

With a functionality of 3 and molecular weight of 6000, this high-activity polyether polyol can be used to produce pavement polyurethane materials, which have a higher tensile strength and resilience.

EP-330N(G)

32.5-35.5

≤0.05

≤0.05

5-7

≤0.07

800-1000

≤3

≤50

With a functionality of 3 and molecular weight of 5000, this high-activity polyether polyol can be used for CASE series products, which have a higher tensile strength and resilience.

 

PPGs for  pavement adhesives

Trademark

Hydroxyl value

mgKOH/g

Acid value

mgKOH/g

Water content

%

pH

Unsaturated value

mol/kg

Viscosity

mPa·s/25℃

K+

mg/kg

Colourity

APHA

Application

Feature

DL-400

270-290

≤0.05

≤0.05

5-7

-

60-80

≤5

≤50

This is a low unsaturated polypropylene oxide ether diol, with a molecular weight of 400-8000.  As the basis component for the soft segment structure of polyurethane, it can be used for a variety of polyurethane adhesive products.

DL series products are mainly used for CASE series products, with a molecular weight range from 700 to 12000. For application, as the molecular weight of the polyol increases, the elongation at break gradually increases while the tensile strength and hardness decreases. Customers may choose polyether polyols of different molecular weight according to their final product’s request. They can also arrange MN-3050DF, EP-330NG or EP-3600 in groups to increase the product’s tensile strength.

DL-700

150-170

≤0.05

≤0.05

5-7

-

80-150

≤10

≤50

DL-1000D

109-115

≤0.05

≤0.02

5-8

-

120-180

-

-

DL-2000D

54.5-57.5

≤0.05

≤0.02

5-8

≤0.01

270-370

-

-

DL-2500D

43-47

≤0.05

≤0.02

5-8

≤0.01

-

-

-

DL-3000D

36-39

≤0.05

≤0.02

5-8

≤0.01

500-600

-

-

DL-4000D

26.5-29.5

≤0.05

≤0.02

5-8

≤0.01

800-1000

-

-

EDL-8000

12.5-15.5

≤0.08

≤0.05

5-8

-

≤5000

-

-

EP-330N(G)

32.5-35.5

≤0.05

≤0.05

5-7

≤0.07

800-1000

≤3

≤50

With a functionality of 3 and molecular weight of 5000, this kind of high-activity polyether polyol can be used for polyurethane adhesive products, which can effectively increase the tensile strength and the resilience.

 

 

PPGs for slurry and soles

Trademark

Hydroxyl value

mgKOH/g

Acid value

mgKOH/g

Water content

%

pH

Unsaturated value

mol/kg

Viscosity

mPa·s/25℃

K+

mg/kg

Colourity

APHA

Application & Feature

ED-28

26.5-29.5

≤0.05

≤0.05

5-7

700-1000

≤5

≤50

With a functionality of 2 and molecular weight of 4000, this high-activity polyether polyol can be used for the preparation of footwear materials, whose elongation at break has been increased, while curing speed increases and stripping time gets shorter.

EP-551C

54.5-57.5

≤0.05

≤0.05

5-7

≤0.05

400-600

≤3

≤50

 

With a functionality of 3 and molecular weight of 3000, this high-activity polyether polyols can be used for the preparation of polyurethane soles materials.

 

 

EP-3600

26.5-29.5

≤0.06

≤0.05

5-7

≤0.08

1000-1600

≤5

≤50

With a functionality of 3 and molecular weight of 6000, this high-activity polyether polyol can be used for the preparation of polyurethane footwear materials, whose resilience has been effectively increased.

 

PPGs for leather finishing agents

Trademark

Hydroxyl value

mgKOH/g

Acid value

mgKOH/g

Water content

%

pH

Viscosity

mPa·s/25℃

Application & Feature

DL-1000D

109-115

≤0.05

≤0.02

5-8

120-180

It is used to produce polyurethane leather finishing agent, with its polymers have good strength, abrasion resistance, solvent resistance and other properties. It has a wide range of applications in rubber, coatings, adhesives, synthetic fibers and other fields, especially as a coating agent used in high-grade leather.

DL-2000D

54.5-57.5

≤0.05

≤0.02

5-8

270-370

MN-3050DF

54.5-57.5

≤0.05

≤0.05

5-7

400-700

 

 

Base PPGs: used in foam sponge for soft furniture

Trademark

Hydroxyl value

mgKOH/g

Acid value

mgKOH/g

Water content

%

pH

Unsaturated value

mol/kg

Viscosity

mPa·s/25℃

K+

mg/kg

Colourity

APHA

Application

Feature

DEP-5631D

54.5-57.5

≤0.05

≤0.05

5-7

≤0.01

400-700

-

-

Low, middle and high density soft block Polyurethane foam for packing and cushion materials.

1. Higher activity than MN-3050D. When produce low density foam ,it less prone to collapse bubbles, cracks and other abnormal defects. 2. with low unsaturated value  and average functionality over 2.9,the foam made by it has higher tensile strength and indentation hardness, and less permanent deformation than traditional soft foam. 3. Has antioxidant of BHT.

DEP-5631ED

54.5-57.5

≤0.05

≤0.05

5-7

≤0.01

400-700

-

-

Without  BHT  and with strong anti-yellow capability

MN-3050D

54.5-57.5

≤0.05

≤0.05

5-7

≤0.01

400-700

 

-

-

Middle and high density soft block polyurethane foams for packing and cushion materials.

1. less activity than DEP-5631D and not fit for low density form. When be used in wide middle and high density foam, it is easier for users to adjust the formula.  2. with low unsaturated value  and average functionality over 2.9,the foam made by it has higher tensile strength and indentation hardness, and less permanent deformation than traditional soft foam. 3. Has antioxidant of BHT.

EP-455S

43.5-46.5

≤0.05

≤0.05

5-7

≤0.05

550-750

≤3

≤50

extra soft block foam for packing, cushion material

PO and EO PPG of 3500 molecular weight. Soft polyurethane block foam made from it could obviously promote softness and comfort

 

POP: used in foam sponge for soft furniture

Trademark

Hydroxyl value

mgKOH/g

Water content

%

PH

Viscosity

mPa·s/25℃

Solid content %

Application & Feature

POP36/28

25-29

≤0.05

6-9

≤3500

23-25

High activity POP with solid content of 24 is used in preparation of high-load flexible Polyurethane foam by mixing with high activity PPG.

POP93/28

23-27

≤0.05

5-8

≤3500

26-28

High activity POP with solid content of 27 is used in preparation of high-load flexible Polyurethane foam by mixing with high activity PPG. The hardening capability is higher than POP 36/28, but is less than HPOP 40.

POP13A

46.5-49.5

 0.1

6-9

800-1200

12-14

 

Solid content of 13.  Used directly in the preparation of common flexible block foams to improve the hardness. It has low viscosity and has good intermiscibility with dichloromethane. Utilization of environmentally friendly catalyst. No tetramethyl-succinonitrile in it so the harm to human body is reduced

POP13A and POP13B have different hydroxyl value and molecular weight. POP 13A is synthesized from base PPG of 3000 molecular weight and fits for Chinese customers. POP 13B is synthesized from base PPG of 3500 molecular weight and fits for European and American customers.

POP13B

39-42

 0.1

6-9

800-1200

12-14

POP45

28.5-31.5

 0.1

6-9

≤8500

43.5-45

1 POP with solid content of 45 is used in the preparation of common block foam to improve the hardness of the foams. It is the most effective POP in term of hardening capability. 2 It has good intermiscibility  with dichloromethane and can be used solely or with other flexible PPG for low, middle and high density foam. 3. Utilization of environmentally friendly catalyst. No tetramethyl-succinonitrile in it so the harm to human body is reduced.

 

Rigid PPGs for insulation materials

Trademark

Hydroxyl value

mgKOH/g

Acid value

mgKOH/g

Water content

%

pH

Viscosity

mPa·s/25℃

K+

mg/kg

Colourity

GD

Application

Feature

SU-450L

440-460

≤0.30

≤0.10

4-6

6000-10000

≤8

≤8

Used in refrigerators, freezers, cold storage and other Polyurethane heat preservation, cold insulation material

With moderate Functionality and viscosity,it is fit for various foaming system solely or with other rigid PPG. Balance between foam mobility and dimensional stability is favorable for Polyurethane heat preservation boards.

Suitable for preparing boards. The functionality, hydroxyl value and viscosity of SU-450L is a bit higher and leads to slightly high compression strengthen and dimension stability. The viscosity of composite material, dimension stability of foam and customer habit decides the application of these two products.

SU-440L

425-455

≤0.20

≤0.10

4-6

4800-6200

≤30

≤8

SA-460

445-475

≤0.50

≤0.10

4-6

11500-16500

≤30

≤5

Good intermiscibility with physical foaming agents . Mixed with other rigid PPG in a variety of  foaming system, especially fit for pentane foaming system. It can improve the compression strength and dimension stability

SA-380 and SA-460 belong to the same class of rigid PPG and fit for pentanes system. Low hydroxyl value and viscosity of SA-380 can improve material mobility. High hydroxyl value and viscosity of SA-460 can improve the compression strengthen and dimension stability. The mixed utilization of them will be better.

SA-380

355-395

≤0.50

≤0.20

-

2000-3000

≤50

≤6

With moderate Functionality and viscosity,it is fit for various foaming system solely or with other rigid PPG. Balance between foam mobility and dimensional stability is favorable for Polyurethane heat preservation boards.

DD-380A

360-400

-

≤0.20

9-12

9000-13000

-

≤9

High functionality rigid PPG. Mixed with other rigid PPG to produce rigid foam heat preservation materials. it can obviously improve compression strengthen and dimension stability, and prevent low-temperature shrinkage of the foam.

DD-4110

430-470

≤0.20

≤0.20

9-12

3000-6000

-

≤8

Used in refrigerators, freezers, cold storage, solar energy, painting, sheet, pipe thermal insulation material.

Classic, Broad-spectrum sucrose rigid PPG  which is the base material of rigid foam, and fits various foaming system with good liquidity and moderate activity

DD-4110Ⅱ

415-445

≤0.20

≤0.20

9-12

2500-3500

-

≤9

Improved low viscosity sucrose rigid PPG which has good mobility and moderate activity, fits for various foaming system, and can be used as base material of rigid Polyurethane foam.

NT-403A

735-805

-

≤0.10

≤13

1400-2400

(50℃)

-

≤50

APHA

Used as heat preservation and cold insulation material in refrigerators, freezers, cold storage, and also used in rigid foam painting, etc

Has high activity and viscosity, fits with various foaming system, and needs to mix with common rigid PPG. Difficult to use solely due to high activity. High viscosity leads to difficult utilization in winter.

 

PPGs for defoamer

Trademark

Hydroxyl value

mgKOH/g

Acid value

mgKOH/g

Water content

%

pH

Viscosity

mPa·s/25℃

K+

mg/kg

Colourity

APHA

Application & Feature

EP-461

48-52

≤0.10

≤0.20

5-7

400-600

≤10

≤50

For the synthesis of polyether defoamer. With its preferable hydrophily, it can easily spread in the foaming medium and has good defoaming ability. Suggest to utilize in viscous fermentation liquid due to its high solubility and short duration of activity.

EP-461-Ⅰ

48-52

≤0.10

≤0.20

5-7

400-600

≤10

≤50

EP-461-Ⅱ

52-56

≤0.10

≤0.20

5-7

-

≤10

≤50

EP-463

53-57

≤0.05

 

≤0.05

 

5-8

-

≤5

≤50

DL-461

46-54

≤0.05

≤0.10

5-7

-

-

≤50

 

PPGs for crosslinking agents

Trademark

Hydroxyl value

mgKOH/g

Acid value

mgKOH/g

Water content

%

pH

Viscosity

mPa·s/25℃

K+

mg/kg

Colourity

APHA

Application

Feature

DV-125

440-460

≤0.08

≤0.08

5-8

300-500

≤8

≤50

Used in crosslinking agents for polyurethane elastomers, rigid foam  crosslinker and foam sealing agent

It can improve the hardness of product when used in crosslinking agents for polyurethane elastomers, reduce the viscosity of blend material for rigid foam crosslingker , enhance the hardness and solidifying speed for foam sealing agent

MN-500

330-350

≤0.08

≤0.05

5-7

-

≤5

≤50

It can improve the hardness of product when used in crosslinking agents for polyurethane elastomers, reduce the viscosity of blend material for rigid foam crosslingker , enhance the hardness and solidifying speed for foam sealing agent

All of them are used as foam sealing agent. MN-500 is good at improving hardness of foam, MN-1000 is good at enhance bonding strength, MN-700’s performance is in the middle of them.

MN-700

225-255

≤0.05

≤0.10

5-7

200-400

≤5

≤50

MN-1000

163-173

≤0.05

≤0.10

5-7

-

≤5

≤50

DL-400

270-290

≤0.05

≤0.05

5-7

60-80

≤5

≤50

Diol PPG with molecular weight of 400 can improve the product toughness when used for  polyurethane elastomer chain extender, and reduce the system viscosity when used for polyurethane grouting material and foam sealing agent

 

Special PPG (1)

Trademark

Hydroxyl value

mgKOH/g

Acid value

mgKOH/g

Water content

%

pH

Unsaturated value

mol/kg

K+

mg/kg

Colourity

APHA

Application

Feature

D-230

480-510

≤0.10

≤0.06

5-7.5

≤0.008

≤6

≤100

Used for the synthesis of amino terminated polyether and various rigid heat preservation material.

2-functional hydroxyl-terminated polypropylene oxide ether with molecular weight of 230 is used in the ammonification synthesis of amino terminated polyether, which can be used as epoxy hardener or Polyurethane chain extender due to low viscosity, high activity and good colourity

EP-8000

22-26

≤0.10

≤0.08

5-7

≤0.15

≤5

≤100

Tri-functional high activity PPG with molecular weight of 8000 is used in various molded foam for auto interior material due to high activity and short demolding time. Polyurethane foam produced from EP-8000 has higher resilience and less hardness than foam from EP-330NY. The pulled strength and resilience can be improved when uses in CASE products.

Higher opening capability than EP-330NY and EP-3600, which may lead to collapse or  excess retraction of foam when preparing TDI and T/M high resilient block foam.

EDL-210

10-12

≤0.10

≤0.05

5-8

-

-

-

Used in polyurethane waterproof coatings, adhesives, elastomers, sports pavement materials.

Low unsaturated polypropylene oxide ether  diol with 12000 molecular weight can be used in CASE products as the base part of soft segment.

T-403

374-390

≤0.10

≤0.10

5-8

≤0.04

≤6

≤50

Used for the synthesis of amino terminated polyether and rigid thermal insulation materials.

Tri-functional hydroxyl-terminated polypropylene oxide ether with molecular weight of 440 is used in the ammonification synthesis of amino terminated polyether, which can be used as Epoxy hardener and polyurethane reacting crosslinking agent due to low viscosity, high activity and good colourity

 

Special PPG (2)

Trademark

Hydroxyl value

mgKOH/g

Acid value

mgKOH/g

Water content

%

pH

Viscosity

mPa·s/25℃

K+

mg/kg

Colourity

APHA

Application

 

Feature

 

DK-12

30-34

≤0.1

≤0.1

5-8

-

≤10

≤100

High resilience opening agent

It can effectively improve the opening capability of high resilient foam which fits for full MDI system or M/T cold molded foam system. Please pay attention to the possible collapse of foam for the preparation of full TDI system or T/M high resilient block foam

EDL-210

10-12

≤0.10 

≤0.05

5-8

-

-

-

Used in polyurethane waterproof coating, adhesive, elastomer, sport pavement material

Low unsaturated polypropylene oxide ether diol with molecular weight of 12000 is used in CASE products as fundamental part of soft segment structure of polyurethane products

LD-801

450-550

-

≤0.10

≥9

1500-4500

-

≤5GD

Specially for rigid polyurethane spray foam thermal insulation material.

Amine rigid PPG with functionality of 3.7 has extremely activity and fits for spray foam system when mixes with common rigid PPG. This product has similar activity as NT-403A but has no dimension stability of latter. Please be careful for the area out of spray

EP-560

290-310

≤0.10 

≤0.05

5-7

-

≤10

≤100

Used for slow rebound foam products

High activity PPG with 3 functionalities and 560 molecular weight can be prepared for slow rebound foam by reacting with PPG of 3 functionalities and 3000 molecular weight and POP when isocyanate index is less than 100

ZR-001

26-30

-

≤0.10

7~9

2000~2600

Solid content: 25-29%

Used in flame-retardant high resilience form, cold molded flexible foam, semi-rigid foam, self-skinning foam, reacting injection molded products, etc

Structural flame-retardant POP can effectively improve the flame retardency and supporting capacity of high resilience foam when mixes with high activity PPG. Comparing with common POP, these two product have extremely higher opening ability. Please mind to aviod the collapse of foam caused by its excessive opening capacity when produce high resilience foam. 

ZR-002

22-28

-

≤0.10

7~10

4000-7000

Solid content: 35-39%

 

 


Keywords:

Polyester Polyols
Related Products
Polyols Series Polyols Series
Polyether Polyols Polyether Polyols
+86 156 3251 6851 +86 150 7632 3255 15033233665 gilbert@houfa-polyurethane.com  james@houfa-newmaterials.com 313011414 1144651831